Presenting Pinku Style line of forged 6061 T6 Aluminum wheels spec'd for the Tesla Cybertruck/Cyberbeast. Stand apart from the bland crowd with full control over your wheel. PDC of 6x139.7, hub bore of 100mm, TPMS valve holes and hub spacing to accept the larger calipers will be as normal for all wheels. All the other factors you can modify yourself.
Notes
The wheel colors seen only serve as examples of what YOU can make. Utilizing the color chip key below, select YOUR color combo to stand out even further from the pack.
(Quantity 1 equals 4 wheels!!!!!)
Manufacturing process for wheels not already built will take 20-30 days on average however can be sooner!! Please contact before purchasing with your full order request from YOUR cart. Express processing can be had for $450usd additional to have the order processed in 15-20 days on average. Check "Order Expedite" above to add to your order.
Professional renders available with your colors of choice from the chart below. The cost is 78.50usd and will take 2-4 business (Mon-Fri non holiday) days to complete.
Please message donald@pinkustyle.com to process pre order render.
Wheels are built to withstand harsh street and track conditions.
A three year service warranty is issued on a case by case bases with investigation. The warranty does not cover racing and or off-road but general daily use.
Wheels are made from high quality, light weight and durable 6061 T6 aluminum billets using JWL/VIA wheel testing ratings.
| Mechanical 6061 T6 Properties/Data | ||||
|
||||
| Hardness, Brinell | 95 | 95 | AA; Typical; 500 g load; 10 mm ball | |
| Hardness, Knoop | 120 | 120 | Converted from Brinell Hardness Value | |
| Hardness, Rockwell A | 40 | 40 | Converted from Brinell Hardness Value | |
| Hardness, Rockwell B | 60 | 60 | Converted from Brinell Hardness Value | |
| Hardness, Vickers | 107 | 107 | Converted from Brinell Hardness Value | |
| Ultimate Tensile Strength | 310 MPa | 45000 psi | AA; Typical | |
| Tensile Yield Strength | 276 MPa | 40000 psi | AA; Typical | |
| Elongation at Break | 12 % | 12 % | AA; Typical; 1/16 in. (1.6 mm) Thickness | |
| Elongation at Break | 17 % | 17 % | AA; Typical; 1/2 in. (12.7 mm) Diameter | |
| Modulus of Elasticity | 68.9 GPa | 10000 ksi | AA; Typical; Average of tension and compression. Compression modulus is about 2% greater than tensile modulus. | |
| Notched Tensile Strength | 324 MPa | 47000 psi | 2.5 cm width x 0.16 cm thick side-notched specimen, Kt = 17. | |
| Ultimate Bearing Strength | 607 MPa | 88000 psi | Edge distance/pin diameter = 2.0 | |
| Bearing Yield Strength | 386 MPa | 56000 psi | Edge distance/pin diameter = 2.0 | |
| Poisson's Ratio | 0.33 | 0.33 | Estimated from trends in similar Al alloys. | |
| Fatigue Strength | 96.5 MPa | 14000 psi | AA; 500,000,000 cycles completely reversed stress; RR Moore machine/specimen | |
| Fracture Toughness | 29 MPa-m½ | 26.4 ksi-in½ | KIC; TL orientation. | |
| Machinability | 50 % | 50 % | 0-100 Scale of Aluminum Alloys | |
| Shear Modulus | 26 GPa | 3770 ksi | Estimated from similar Al alloys. | |
| Shear Strength | 207 MPa | 30000 psi | AA; Typical | |
|
||||
| Electrical Resistivity | 3.99e-006 ohm-cm | 3.99e-006 ohm-cm | AA; Typical at 68°F | |
Thermal Properties |
||||
|
||||
| CTE, linear 68°F | 23.6 µm/m-°C | 13.1 µin/in-°F | AA; Typical; Average over 68-212°F range. | |
| CTE, linear 250°C | 25.2 µm/m-°C | 14 µin/in-°F | Estimated from trends in similar Al alloys. 20-300°C. | |
| Specific Heat Capacity | 0.896 J/g-°C | 0.214 BTU/lb-°F | ||
| Thermal Conductivity | 167 W/m-K | 1160 BTU-in/hr-ft²-°F | AA; Typical at 77°F | |
| Melting Point | 582 - 652 °C | 1080 - 1205 °F | AA; Typical range based on typical composition for wrought products 1/4 inch thickness or greater; Eutectic melting can be completely eliminated by homogenization. | |
| Solidus | 582 °C | 1080 °F | AA; Typical | |
| Liquidus | 652 °C | 1205 °F | AA; Typical | |
Processing Properties |
||||
|
||||
| Solution Temperature | 529 °C | 985 °F | ||
| Aging Temperature | 177 °C | 350 °F | Extrusions or forgings; hold at temperature for 8 hr | |